Analysis of Product Defects by Lifting Hook Manufacturers
Commonly used lifting accessories and tools include jacks, reverse chains, clamping rings, ropes, hooks, hand-held hoists, crimping mills, pulleys and pulley sets. Holding hooks are key components in lifting and transportation machinery. The hooks are often made of low-carbon steel, low-alloy steel ingots and steels of low-alloy steel through free forging or molds. Quality is crucial. Due to the hook forging process, its geometry is limited, so different hooks may have certain defects. Next, let’s take a look at the introduction of the hoisting hook manufacturer:
The casting defects mainly include residual shrinkage holes, looseness, slag inclusions, and cracks. Forging defects include: folding, white dots, and cracks. The main heat treatment defects include cracks, crude products, etc.
In order to avoid the above defects causing serious consequences for subsequent processing, the lifting hook needs to be flaw detection after processing is completed, and in addition to heat treatment. Our company's products mainly include: pulley sets, hook sets, wheel sets, cable drums, electric hoists, chain hoists, electromagnetic suction cups, etc. The products are well used in metallurgy, mechanical processing and other fields. If you are interested in our products, please contact our manufacturer.
Commonly used lifting accessories and tools include jacks, reverse chains, clamping rings, ropes, hooks, hand-held hoists, crimping mills, pulleys and pulley sets. Holding hooks are key components in lifting and transportation machinery. The hooks are often made of low-carbon steel, low-alloy steel ingots and steels of low-alloy steel through free forging or molds. Quality is crucial. Due to the hook forging process, its geometry is limited, so different hooks may have certain defects. Next, let’s take a look at the introduction of the hoisting hook manufacturer:
The casting defects mainly include residual shrinkage holes, looseness, slag inclusions, and cracks. Forging defects include: folding, white dots, and cracks. The main heat treatment defects include cracks, crude products, etc.
In order to avoid the above defects causing serious consequences for subsequent processing, the lifting hook needs to be flaw detection after processing is completed, and in addition to heat treatment. Our company's products mainly include: pulley sets, hook sets, wheel sets, cable drums, electric hoists, chain hoists, electromagnetic suction cups, etc. The products are well used in metallurgy, mechanical processing and other fields. If you are interested in our products, please contact our manufacturer.
Commonly used lifting accessories and tools include jacks, reverse chains, clamping rings, ropes, hooks, hand-held hoists, crimping mills, pulleys and pulley sets. Holding hooks are key components in lifting and transportation machinery. The hooks are often made of low-carbon steel, low-alloy steel ingots and steels of low-alloy steel through free forging or molds. Quality is crucial. Due to the hook forging process, its geometry is limited, so different hooks may have certain defects. Next, let’s take a look at the introduction of the hoisting hook manufacturer:
The casting defects mainly include residual shrinkage holes, looseness, slag inclusions, and cracks. Forging defects include: folding, white dots, and cracks. The main heat treatment defects include cracks, crude products, etc.
In order to avoid the above defects causing serious consequences for subsequent processing, the lifting hook needs to be flaw detection after processing is completed, and in addition to heat treatment. Our company's products mainly include: pulley sets, hook sets, wheel sets, cable drums, electric hoists, chain hoists, electromagnetic suction cups, etc. The products are well used in metallurgy, mechanical processing and other fields. If you are interested in our products, please contact our manufacturer.