Safety inspection and testing standards for crane hooks

2025-07-28 14:20:17

crane hooks are key load-bearing components of lifting equipment, and their safety is directly related to the safety of operators and equipment. To ensure the safe use of hooks, daily inspections, regular tests and scrapping standards must be strictly implemented and in compliance with international/national standards (such as ISO, ASME, OSHA, etc.). The following are detailed safety inspection and testing specifications.


1. Daily inspection (operator's responsibilities)

Inspection frequency : before each use or before each shift.
Inspection method : visual inspection + manual test.

1. Check the content

Inspection items Eligibility criteria Substandard performance
Overall appearance of hook No cracks, deformation or rust Visible cracks, severe rust, obvious bending
Throat Opening ≤ 10% of original size (refer to ISO 2415) Deformation exceeds 10% or hook tip is severely worn
Anti-unhooking device (Latch) Flexible and reliable, no spring failure Stuck, broken, unable to close automatically
Thread and pin No damage, no looseness Thread stripping, pin deformation or excessive wear
Hook rotation Flexible rotation without jamming Bearing damage, difficult to rotate

2. Check tools

  • Flashlight (to check for internal cracks)

  • Caliper (to measure hook deformation)

  • Non-metallic hammer (tap lightly and listen to the sound to determine internal defects)

Dealing with discovered problems :

  • Immediately deactivate and mark "Danger, Do Not Use".

  • Report for repair or replacement.


2. Regular testing (professional and technical personnel)

Testing frequency :

  • Monthly testing (high risk environments such as metallurgy, ports).

  • Annual comprehensive inspection (including NDT, in accordance with OSHA/ASME requirements).

1. Test items and methods

Test items Detection Methods Standard basis
Static load test Apply 200% WLL for 5 minutes (ASME B30.10) No permanent deformation, cracks (ISO 7597)
Magnetic Particle Testing (MT) Detect surface cracks (focus: hook throat, thread root) ASTM E1444 / ISO 4986
Ultrasonic Testing (UT) Detection of internal defects (pores, inclusions) ASTM E2375 / ISO 7963
Hardness test Ensure hardness is HB 300-400 (ISO 2415) Rockwell hardness tester (HRC 30-40)
Dimensional Measurement Whether the hook mouth and hook throat dimensions conform to the original design Calipers, coordinate measuring machines

2. Test report requirements

  • Record the test date, tester, test method, and results.

  • Retain for at least 3 years (OSHA 1910.179 requirement).


3. Scrapping Standard (Immediate Replacement)

If the hook has the following conditions, it must be scrapped :

Defect Type Scrap Standard Reference Specifications
crack Any visible cracks (regardless of length) ASME B30.10 / ISO 2415
Hook deformation The opening exceeds the original size by 15% OSHA 1926.550
Hook tip wear Section loss ≥ 10% EN 1677-1
Thread damage Thread slippage and deformation affect the tightening of the nut ISO 898-1 (8.8 grade bolt standard)
Severe rust Affecting structural strength (such as deep corrosion ≥ 1mm) ASTM A668

4. Comparison of International Testing Standards

standard Testing requirements Applicable regions
ASME B30.10 200% WLL static load test + MT/UT test United States, Canada
ISO 2415 200% WLL test + hardness check EU, Middle East, Asia
EN 1677-1 Magnetic particle inspection + dimensional tolerance inspection Europe (CE certification)
GB/T 10051 150% WLL test + appearance inspection China

5. Best Practices

  1. Create an inspection checklist (refer to OSHA 1910.179 Appendix A).

  2. Use smart inspection tools (such as ultrasonic thickness gauges, industrial endoscopes).

  3. Train operators (OSHA 1926.1427 requires certification).

  4. Digital management (recording test data and achieving traceability).


in conclusion

  • Daily inspections prevent sudden failures, and regular testing ensures long-term safety.

  • Strictly implement scrapping standards to avoid accidents caused by hook failure.

  • Meets OSHA/ASME/ISO standards to ensure compliance in global markets.

Immediate actions :
✅ Develop an inspection plan
✅ Train relevant personnel
✅ Introduce NDT testing equipment (such as portable magnetic particle flaw detector)

Crane hooks are key load-bearing components of lifting equipment, and their safety is directly related to the safety of operators and equipment. To ensure the safe use of hooks, daily inspections, regular tests and scrapping standards must be strictly implemented and in compliance with international/national standards (such as ISO, ASME, OSHA, etc.). The following are detailed safety inspection and testing specifications.


1. Daily inspection (operator's responsibilities)

Inspection frequency : before each use or before each shift.
Inspection method : visual inspection + manual test.

1. Check the content

Inspection items Eligibility criteria Substandard performance
Overall appearance of hook No cracks, deformation or rust Visible cracks, severe rust, obvious bending
Throat Opening ≤ 10% of original size (refer to ISO 2415) Deformation exceeds 10% or hook tip is severely worn
Anti-unhooking device (Latch) Flexible and reliable, no spring failure Stuck, broken, unable to close automatically
Thread and pin No damage, no looseness Thread stripping, pin deformation or excessive wear
Hook rotation Flexible rotation without jamming Bearing damage, difficult to rotate

2. Check tools

  • Flashlight (to check for internal cracks)

  • Caliper (to measure hook deformation)

  • Non-metallic hammer (tap lightly and listen to the sound to determine internal defects)

Dealing with discovered problems :

  • Immediately deactivate and mark "Danger, Do Not Use".

  • Report for repair or replacement.


2. Regular testing (professional and technical personnel)

Testing frequency :

  • Monthly testing (high risk environments such as metallurgy, ports).

  • Annual comprehensive inspection (including NDT, in accordance with OSHA/ASME requirements).

1. Test items and methods

Test items Detection Methods Standard basis
Static load test Apply 200% WLL for 5 minutes (ASME B30.10) No permanent deformation, cracks (ISO 7597)
Magnetic Particle Testing (MT) Detect surface cracks (focus: hook throat, thread root) ASTM E1444 / ISO 4986
Ultrasonic Testing (UT) Detection of internal defects (pores, inclusions) ASTM E2375 / ISO 7963
Hardness test Ensure hardness is HB 300-400 (ISO 2415) Rockwell hardness tester (HRC 30-40)
Dimensional Measurement Whether the hook mouth and hook throat dimensions conform to the original design Calipers, coordinate measuring machines

2. Test report requirements

  • Record the test date, tester, test method, and results.

  • Retain for at least 3 years (OSHA 1910.179 requirement).


3. Scrapping Standard (Immediate Replacement)

If the hook has the following conditions, it must be scrapped :

Defect Type Scrap Standard Reference Specifications
crack Any visible cracks (regardless of length) ASME B30.10 / ISO 2415
Hook deformation The opening exceeds the original size by 15% OSHA 1926.550
Hook tip wear Section loss ≥ 10% EN 1677-1
Thread damage Thread slippage and deformation affect the tightening of the nut ISO 898-1 (8.8 grade bolt standard)
Severe rust Affecting structural strength (such as deep corrosion ≥ 1mm) ASTM A668

4. Comparison of International Testing Standards

standard Testing requirements Applicable regions
ASME B30.10 200% WLL static load test + MT/UT test United States, Canada
ISO 2415 200% WLL test + hardness check EU, Middle East, Asia
EN 1677-1 Magnetic particle inspection + dimensional tolerance inspection Europe (CE certification)
GB/T 10051 150% WLL test + appearance inspection China

5. Best Practices

  1. Create an inspection checklist (refer to OSHA 1910.179 Appendix A).

  2. Use smart inspection tools (such as ultrasonic thickness gauges, industrial endoscopes).

  3. Train operators (OSHA 1926.1427 requires certification).

  4. Digital management (recording test data and achieving traceability).


in conclusion

  • Daily inspections prevent sudden failures, and regular testing ensures long-term safety.

  • Strictly implement scrapping standards to avoid accidents caused by hook failure.

  • Meets OSHA/ASME/ISO standards to ensure compliance in global markets.

Immediate actions :
✅ Develop an inspection plan
✅ Train relevant personnel
✅ Introduce NDT testing equipment (such as portable magnetic particle flaw detector)

Crane hooks are key load-bearing components of lifting equipment, and their safety is directly related to the safety of operators and equipment. To ensure the safe use of hooks, daily inspections, regular tests and scrapping standards must be strictly implemented and in compliance with international/national standards (such as ISO, ASME, OSHA, etc.). The following are detailed safety inspection and testing specifications.


1. Daily inspection (operator's responsibilities)

Inspection frequency : before each use or before each shift.
Inspection method : visual inspection + manual test.

1. Check the content

Inspection items Eligibility criteria Substandard performance
Overall appearance of hook No cracks, deformation or rust Visible cracks, severe rust, obvious bending
Throat Opening ≤ 10% of original size (refer to ISO 2415) Deformation exceeds 10% or hook tip is severely worn
Anti-unhooking device (Latch) Flexible and reliable, no spring failure Stuck, broken, unable to close automatically
Thread and pin No damage, no looseness Thread stripping, pin deformation or excessive wear
Hook rotation Flexible rotation without jamming Bearing damage, difficult to rotate

2. Check tools

  • Flashlight (to check for internal cracks)

  • Caliper (to measure hook deformation)

  • Non-metallic hammer (tap lightly and listen to the sound to determine internal defects)

Dealing with discovered problems :

  • Immediately deactivate and mark "Danger, Do Not Use".

  • Report for repair or replacement.


2. Regular testing (professional and technical personnel)

Testing frequency :

  • Monthly testing (high risk environments such as metallurgy, ports).

  • Annual comprehensive inspection (including NDT, in accordance with OSHA/ASME requirements).

1. Test items and methods

Test items Detection Methods Standard basis
Static load test Apply 200% WLL for 5 minutes (ASME B30.10) No permanent deformation, cracks (ISO 7597)
Magnetic Particle Testing (MT) Detect surface cracks (focus: hook throat, thread root) ASTM E1444 / ISO 4986
Ultrasonic Testing (UT) Detection of internal defects (pores, inclusions) ASTM E2375 / ISO 7963
Hardness test Ensure hardness is HB 300-400 (ISO 2415) Rockwell hardness tester (HRC 30-40)
Dimensional Measurement Whether the hook mouth and hook throat dimensions conform to the original design Calipers, coordinate measuring machines

2. Test report requirements

  • Record the test date, tester, test method, and results.

  • Retain for at least 3 years (OSHA 1910.179 requirement).


3. Scrapping Standard (Immediate Replacement)

If the hook has the following conditions, it must be scrapped :

Defect Type Scrap Standard Reference Specifications
crack Any visible cracks (regardless of length) ASME B30.10 / ISO 2415
Hook deformation The opening exceeds the original size by 15% OSHA 1926.550
Hook tip wear Section loss ≥ 10% EN 1677-1
Thread damage Thread slippage and deformation affect the tightening of the nut ISO 898-1 (8.8 grade bolt standard)
Severe rust Affecting structural strength (such as deep corrosion ≥ 1mm) ASTM A668

4. Comparison of International Testing Standards

standard Testing requirements Applicable regions
ASME B30.10 200% WLL static load test + MT/UT test United States, Canada
ISO 2415 200% WLL test + hardness check EU, Middle East, Asia
EN 1677-1 Magnetic particle inspection + dimensional tolerance inspection Europe (CE certification)
GB/T 10051 150% WLL test + appearance inspection China

5. Best Practices

  1. Create an inspection checklist (refer to OSHA 1910.179 Appendix A).

  2. Use smart inspection tools (such as ultrasonic thickness gauges, industrial endoscopes).

  3. Train operators (OSHA 1926.1427 requires certification).

  4. Digital management (recording test data and achieving traceability).


in conclusion

  • Daily inspections prevent sudden failures, and regular testing ensures long-term safety.

  • Strictly implement scrapping standards to avoid accidents caused by hook failure.

  • Meets OSHA/ASME/ISO standards to ensure compliance in global markets.

Immediate actions :
✅ Develop an inspection plan
✅ Train relevant personnel
✅ Introduce NDT testing equipment (such as portable magnetic particle flaw detector)